The aim of this study was to compare the compositions and cytotoxicity of white ProRoot MTA (white mineral trioxide aggregate) and 3 kinds of Portland cements. The elements, simple oxides and phase compositions of white MTA (WMTA), gray Portland cement (GPC), white Portland cement (WPC) and fast setting cement (FSC) were measured by inductively coupled plasma atomic emission spectrometry (ICP-AES), X-ray fluorescence spectrometry (XRF) and X-ray diffractometry (XRD). Agar diffusion test was carr

Mineral trioxide aggregate (MTA) is mainly composed of lime and silica. Its four major phases are tricalcium silicate, dicalcium silicate, tricalcium aluminate, and tetracaclcium aluminoferrite. MTA has relatively long initial setting time (2h 45m)and various additives can be added to reduce setting time. Compressive strength of MTA increases with time and reaches 100 MPa after 28 days. MTA has high pH of 9-12.5 because of the formation of calcium hydroxide during its hydration reaction. MTA has

본 연구의 목적은 Super-EBA, MTA, Dyract-flow를 근관 역충전재로 사용하였을 때의 근단부 폐쇄 능력을 전기화학적 방법을 통해 알아보고자 하는 것이다. 48개의 단근치를 Profile을 사용하여 근관형성한 후, Gutter-percha cone으로 수직가압 충전을 시행하였다. 근단부에서 3mm 되는 부위를 bur로 절단한 후, ultrasonic device로 3mm 깊이의 역충전 와동을 형성하였다. 각 실험군은 Super-EBA, MTA, 혹은 Dyract-flow로 역충전하고 4주에 걸쳐 전기화학적인 방법으로 치근단 누출의 변화를 측정한 후, Repeated measures of ANOVA로 통계분석하였다. 그 결과 모든 시편에서 시간에 따른 치근단 누출의 증가가 관찰되었으나, 각 실험군 간에 누출의 차이는 나타나지 않았다. 이러한 결과는 Dyract-flow의 치근단 역충전재로써의 사용 가능성을 시사한다.

MTAD의 치근단 누출에 미치는 영향에 대한 전기화학적 연구목적: 새로이 개발된 근관세정제 (MTAD)가 근관 충전이 이루어지고 난 치근단 누출에 미치는 영향을 평가해 보고자 하였다. 방법: 일반적인 방법의 근관 성형과 세정 그리고 충전을 시행하는데 있어 실험군 들에서는 NaOCl만, NaOCl 과 EDTA, NaOCl과 MTAD를 사용하였고 10일 동안 표준전극과 시편 근관 내에 위치시킨 실험전극 사이의 전기저항을 측정하여 시간에 따른 치근단 누출의 변화를 비교 평가하였다.결과: 측정 시간 30분에서 7일 사이에서 smear layer 제거한 군들 (Group4와 5)에서 제거하지 않은 군(Group 3)에서 보다 적은 치근단 누출을 보였지만 통계학적인 유의성있는 차이를 나타내지는 않았다. 실험군들 사이에서 모든 시간 대에 걸쳐 치근단 누출의 유의성 있는 차이를 관찰할 수 없었다.

The aim of this study was to investigate the effect of the hybrid instrumentation method with ProTaper and ProFile on the change of root canal area and distance from the canal to the root surface after canal shaping. The mesial canals of twenty extracted mandibular first molars having 10-20°Delta curvature were scanned using X-ray microcomputed tomography (XMCT)-scanner before root canals were instrumented. They were divided into four groups (n=10 canals ter group). In Group 1, root canals were

Injectable calcium phosphate cement (CPC) has been used as bone substitute successfully due to good biocompatibility and osteoconductivity. One of the important mechanical characteristics of CPC is flowablility, which can be evaluated by measuring rheological parameters. However, there have been few studies that measured rheological properties of CPC. The purpose of this study was to evaluate the effects of temperature and concentrations of 2 kinds of setting solutions, hydroxyprophyl methylcell

Calcium phosphate cement (CPC)는 우수한 생체 친화성을 바탕으로 치과 및 의과 쪽에서 성공적인 bone substitute로 사용되어 왔다. 긴 경화시간 및 washout tendency 등 CPC의 단점을 개선하기 위해 다양한 종류의 경화액 및 첨가제등에 대한 연구가 이루어졌다. 그러나 첨가제의 종류에 따른 CPC paste의 점탄성을 정량적으로 비교한 연구는 많지 않다. 이 연구에서는 2% hydroxyprophyl methylcellulose (HPMC)와 35% polyacrylic acid (PAA)의 두 가지 경화액과 혼합된 CPC의 유변학적 성질을 관찰하고 비교하고자 하였다. Dicalcium phosphate dihydrate (DCPD)를 2% HPMC 및 35% PAA와 각각 1:1의 분액비로 30초간 섞은 후 cone and plate geometry를 가지는 rheometer를 사용하여 frequency sweep test와 time

The purpose of this study was to evaluate the contact angle made by 3 kinds of self etching primers (Clearfil SE Bond, AdheSE, and Tyrian) on dentin and to measure the microtensile bond strength of resin composite to dentin using these self-etching primers. Contact angle between each of 3 self etching primers and polished dentin surface was measured (n=30) by contact angle analyzer and the result was analyzed by One-way ANOVA. For the measurement of microtensile bond strength, polished denti

The purpose of this study was to evaluate the effect of the Nd : YAG laser on the tooth hypersensitivity by the observation of the morphological changes of the dentinal surface irradiated with Nd : YAG laser by use of SEM. In 40 mandibular and maxillary molars without any carious lesion or restoration, severe attrition and abrasion, Enamel was removed with fine grit diamond bur and exposed dentinal surfaces were polished with Soflex discs. In control group (10 teeth), exposed dentinal surfaces w

The purpose of this study was to evaluate the effects of MTAD, EDTA and sodium hypochlorite(NaOCl) as final irrigants on coronal leakage resistance to Enterococcus faecalis. Forty extracted human maxillary molars were used in this experiment. The teeth were randomly divided into positive control group (Group 1; n = 5), negative control group (Group 2; n = 5) and three experimental groups (n = 30). In Group 3 (n = 10), the root canals were irrigated with sodium hypochlorite. In Group 4 (n = 10) a

※이 연구는 삼성생명과학연구소 연구비(C-A2-3101)의 보조로 이루어졌음.대한치과보존학회지:Vol. 27, No. 5, 2002464

anaerobic bacterial leakage model을 이용한 음파와 초음파 치근단 와동 형성 기구에 대한 비교

치근부 민감상 ( hypersensitivity )은 부분적으로는 치근면에서의 개방된 상아세관이 존재하는 것에 기인한다고 생각되며 이러한 치근부의 개방된 상아세관은 치경부 병소 (cervical lesion)에 주로 존재하는데 이는 칫솔질에 의한 마모 (toothbrush abrasion), 화학적 침식 (chemical erosion), 또는 abfraction 등의 결과로 나타난다고 한다. 이미 Nd-YAG 레이저를 이용한 실험에서 레이저를 조사한 상아질 표면의 상아 세관 구경이 감소되고 상아세관의 폐쇄가 많이 증가되는 양상을 관찰한 바 있다. 이 실험의 목적은 고출력레이저인 Nd-YAG 레이저를 이용한 상아질표면처치의 임상사용가능성을 좀 더 상세히 평가하기위해 상아질에 레이저를 처리한 후 기계적으로 마모 시킨 경우 상아질 표면의 변화를 관찰하는 것이다. 50개의 발치된 치아의 상아질을 노출시켜 표면을 연마한 후 대조군에서는 37% 인산으로 산부식시켜 상아 세관을 노출시킨 후 레

이 연구의 목적은 이중 중합 복합레진과 수평 포스트를 이용하여 수복한 치관-치근 복합파절 치아의 수직파절 저항성을 알아보기 위한 것이다. 48개의 발치된 사람의 소구치에 실험적으로 치관-치근 복합파절을 일으킨 후 대조군 및 3개의 실험군에 (n=12) 각각 할당하였다. 대조군에서는 치아 파절편을 레진시멘트를 이용하여 접착한 후 근관치료를 시행하고, 근관와동을 이중중합 복합레진을 사용하여 충전하였다. 실험군에서는, 각각의 치아에 근관치료를 시행한 후 레진-포스트 군에서는 근관와동을 수평 포스트 및 이중중합 복합레진을 사용하여 충전하였다. 레진 군에서는 근관와동을 포스트 없이 이중중합 복합레진만 사용하여 수복하였으며 아말감 코어 군에서는 근관와동을 접착 아말감을 사용하여 수복하였다. 이렇게 수복된 치아를 처음과 같은 방법으로 다시 치관-치근 복합파절을 유도하여 이때의 파절 저항성을 기록하고 이 값과 처음 파절을 유도하였을 때의 파절 저항성의 비를 계산하고 각 군별로 차이가 있는 지 검증