Hong Gi Kim

Globally, concrete is the most widely used construction material. The composition of concrete plays an important role in controlling its overall performance. Concrete is composed of approximately 70%-80% aggregates, by volume. Therefore, it is mandatory to investigate the effect of aggregates on the performance of concrete. For this purpose, this study investigated the effect of three different coarse aggregates on the mechanical properties, durability, and microstructure of concrete. Concrete s

In this study, the effects of titanium dioxide (TiO₂) nanoparticles on the sulfate attack resistance of ordinary Portland cement (OPC) and slag-blended mortars were investigated. OPC and slag-blended mortars (OPC:Slag = 50:50) were made with water to binder ratio of 0.4 and a binder to sand ratio of 1:3. TiO₂ was added as an admixture as 0%, 3%, 6%, 9% and 12% of the binder weight. Mortar specimens were exposed to an accelerated sulfate attack environment. Expansion, changes in mass and surface

This study investigates the potential of light-burnt dolomite (LBD) as a supplementary cementitious material with ground granulated blast furnace slag (GGBFS) and Ordinary Portland cement (OPC). In this work, LBD was substituted for up to 20% of GGBFS in sodium sulfate-activated slag systems. The effects of LBD incorporation on the flow, setting time, compressive and flexural strength development, and drying shrinkage were explored with, X-ray diffraction and thermogravimetric analyses. LBD inco

The worldwide production of cement is growing every year due to its increased use in the construction. Cement production is affiliated with an environmental concern as it contributes to the CO2 emissions. It is imperative to reduce the cement production by incorporating supplementary cementitious materials in the cement composites. In this research study, wheat straw ash (WSA) was used as an alternate of ordinary Portland cement. The ash was ground separately with a ball mill and a disintegrator

In this paper, the effect of nano-SiO₂ (NS) and MgO on the hydration characteristics and anti-washout resistance of non-dispersible underwater concrete (UWC) was evaluated. A slump flow test, a viscosity test, and setting time measurement were conducted to identify the impacts of NS and MgO on the rheological properties of UWC. The pH and turbidity were measured to investigate the anti-washout performance of UWC mixes. To analyze the hydration characteristics and mechanical properties

The purpose of this study was to prevent early age autogenous shrinkage in high-strength mortars with saturated tea waste particles. In general, high strength and high performance concretes are made with low water/binder ratios; hence, they are susceptible to shrink at early ages. This shrinkage occurs due to self-desiccation that leads to autogenous shrinkage. To overcome self-desiccation problems in high-strength cement composites, it is necessary to keep the composites moist for a long time.

Increasing use of cement in the construction industry is causing an alarming increase in carbon dioxide (CO₂) emissions, which is a serious environmental threat, it can be reduced by the addition of supplementary cementitious materials (SCMs). The commonly used SCMs like ground granulated blast furnace slag (GGBS), metakaolin (MK) and fly ash (FA) have been successfully used to replace the cement partially or completely. Polysilicon sludge obtained from the photovoltaic industry is al