Hong‐Seok Moon

The present study was intended to investigate changes in the microstructure and phase transformation of zirconia surfaces using etching and airborne-particle abrasion (AB) and the effects of these processes on the shear bond strength of dental resin cements to zirconia. Four groups were classified according to the surface treatment as follows: etching for 15 min (ET15), etching for 30 min (ET30), AB, and etching for 15 min following AB (ABET). These groups were then classified into two subgroups

The purpose of this study was to compare and evaluate, through histomorphometric and radiological analysis, the effects of UV photofunctionalization on an implant placed over a critical defect area with and without a bone graft. Four female beagle dogs were first divided into control and bone graft groups. Each group was then subdivided into UV-treated and UV-untreated groups. The mandibular premolars in each dog were extracted. 12 weeks after extraction, implants were placed according to the co

Abstract The interface between yttrium oxide partially stabilized tetragonal zirconia polycrystalline (Y‐TZP) core and veneering porcelain is the site of most clinical failures. Many efforts have focused on increasing the bond strength between Y‐TZP core and veneering porcelain, and such approaches include increasing the surface roughness and providing undercuts. However, each surface roughening method carries limitations. The specific aim of this study was to test the bond strengths of Y‐TZP su

We evaluated and compared ultraviolet (UV) treatment and simvastatin (SIM) immersion effects on the osseointegration of sandblasted, large-grit, acid-etched (SLA) titanium dental implants at two different time points in rabbit tibias, with or without xenogenic bone graft materials. The surface alteration on simvastatin treatment titanium discs was analyzed using an infrared spectrometer. Implants were categorized into four groups according to the surface treatment type. Twelve rabbits received t

The purpose of this study was to compare the internal gap between CAD/CAM palladium-silver crowns and cast gold crowns generated from intraoral digital versus conventional impressions and to determine the clinical acceptability. Nickel-chrome master dies were made from the prepared resin tooth with the conventional impression method (<i>n</i> = 40). For ICC (Intraoral, CAD/CAM) group, 10 intraoral digital impressions were made, and 10 CAD/CAM crowns of a PD-AG (palladium-silver) machinable alloy

The accuracy of computer-aided design differed according to the type of computer-aided design program. Dental System™ achieved the best trueness at the margins, axial walls, and occlusal surface, followed by Exocad and inLab 16.

Adhesion of zirconia is difficult; thus, etching agents using several different methods are being developed. We investigated the effects of surface treatment with commercially available etching agents on the bond strength between zirconia and resin cement and compared them with those achieved using air abrasion alone. We used 100 zirconia blocks, of which 20 blocks remained untreated, 20 blocks were sandblasted, and 60 blocks were acid-etched using three different zirconia-etching systems: Zirco

The aim of this work was to evaluate the effects of application time of an acid mixture solution on the surface roughness, phase transformation, and biaxial flexural strength of 3Y-TZP after sintering or air abrasion. For the biaxial flexural strength measurement, 220 3Y-TZP disk-shaped specimens were prepared after as-sintering or air abrasion. The etching solution comprised a mixture of hydrofluoric acid, sulfuric acid, hydrogen peroxide, methyl alcohol, and purified water. The samples were di