Mitsuyoshi Akiyama

After recent large earthquakes, field investigations confirmed that several bridges were severely damaged and collapsed not only due to the earthquake, as an independent hazard, but also to the subsequent tsunami, landslide or fault displacement. In addition, long-term material deterioration might have an important impact on seismic damage to bridges. Therefore, it is important to study both independent and interacting hazards and their effects on the reliability and risk of bridges and bridge n

Abstract Over the last two decades, the probabilistic assessment of reinforced concrete (RC) structures under seismic hazard has been developed rapidly. However, little attention has been devoted to the assessment of the seismic reliability of corroded structures. For the life‐cycle assessment of RC structures in a marine environment and earthquake‐prone regions, the effect of corrosion due to airborne chlorides on the seismic capacity needs to be taken into consideration. Also, the effect of th

In this paper, the hazard curve associated with airborne chlorides in a marine environment and the computational procedure to obtain the probability of occurrence of corrosion cracking in reinforced concrete (RC) structures are presented. A method for integration of the effects of airborne chloride into reliability-based durability design of RC structures in a marine environment is proposed. By using this method, it is possible to determine the probability of corrosion cracking due to airborne c

To develop disaster mitigation measures in coastal regions affected by earthquakes, it is important to consider the effects of both seismic and tsunami hazards on road structures and assess the social impacts associated with the economic loss and reduction in network functionality. In this paper, a risk- and resilience-based assessment framework is established for road networks under both seismic and tsunami hazards. In the proposed methodology, the risk and resilience are quantified by the econ

The probabilistic estimation of tsunami impact on bridges and the evaluation of potential tsunami risk are important topics, but they are still in very early stages of development. First, this paper presents the damage of bridges during the great Tohoku‐oki earthquake and giant tsunami of 11 March 2011 based on the field damage investigation. The damage conditions and the possible failure mechanisms of bridges due to tsunami are particularly discussed. Second, tsunami fragility curves are presen

The material properties of concrete structures and their structural dimensions are known to be random due to the spatial variability associated with workmanship and various other factors. This randomness produces spatially variable corrosion damages, such as steel weight loss and corrosion cracks. The structural capacity of reinforced concrete (RC) members strongly depends on the local conditions of their reinforcements. Modelling the spatial variability of steel corrosion is important, but stee

Corrosion-induced crack width can provide effective information on the deterioration level of in situ corroded reinforced concrete (RC) structures. However, the uncertainty associated with the relationship between corrosion-induced crack width and steel corrosion in RC structures is quite large. In this study, a probabilistic framework for estimating the structural capacity of corroded RC structures using the observational corrosion-induced crack width distribution and machine learning is propos

AbstractEven though accurate structural models have been developed for the performance of corroded structures subjected to monotonic flexure and/or shear, studies on seismic performance that include corrosion damage are scarce. For the lifetime assessment of structures in aggressive environments and earthquake-prone regions, the effects of corrosion on seismic performance need to be taken into consideration. Whereas the seismic demand depends on the results of seismic hazard assessment, the dete

Although several models are available for evaluating the structural performance of corroded reinforced concrete (RC) structures, seismic reliability assessments considering the effect of steel corrosion are currently scarce. Determining how long existing RC structures in an aggressive environment will be able to have a seismic safety level greater than the threshold remains difficult. Life-cycle reliability assessments of these structures under seismic hazards and hazards associated with airborn