Jong‐Heun Lee 교수

Abstract The humidity dependence of the gas‐sensing characteristics in SnO 2 ‐based sensors, one of the greatest obstacles in gas‐sensor applications, is reduced to a negligible level by NiO doping. In a dry atmosphere, undoped hierarchical SnO 2 nanostructures prepared by the self‐assembly of crystalline nanosheets show a high CO response and a rapid response speed. However, the gas response, response/recovery speeds, and resistance in air are deteriorated or changed significantly in a humid at

The selective detection of two different gases, NO(2) and C(2)H(5)OH, has been achieved using a p-type Co(3)O(4)-decorated n-type ZnO nanowire (NW) network sensor. The gas selectivity was explained by the catalytic effect of nanocrystalline Co(3)O(4) and the extension of the electron depletion layer via the formation of p-n junctions.

Ammonia (NH₃) is an irritant gas with a unique pungent odor; sub-parts per million-level breath ammonia is a medical biomarker for kidney disorders and Helicobacter pylori bacteria-induced stomach infections. The humidity varies in both ambient environment and exhaled breath, and thus humidity dependence of gas-sensing characteristics is a great obstacle for real-time applications. Herein, flexible, humidity-independent, and room-temperature ammonia sensors are fabricated by the therm

The humidity dependence of the gas sensing characteristics of metal oxide semiconductors has been one of the greatest obstacles for gas sensor applications during the last five decades because ambient humidity dynamically changes with the environmental conditions. Herein, a new and novel strategy is reported to eliminate the humidity dependence of the gas sensing characteristics of oxide chemiresistors via dynamic self-refreshing of the sensing surface affected by water vapor chemisorption. The

Ultraselective and sensitive detection of xylene and toluene with minimum interferences of other indoor air pollutants such as benzene, ethanol, and formaldehyde is achieved using NiO hierarchical nanostructures doped with Cr. Pure and 1.15–2.56 at% Cr-doped NiO flower-like hierarchical nanostructures assembled from nanosheets are prepared by a simple solvothermal reaction and their gas sensing characteristics toward o-xylene and toluene gases are investigated. The 1.15 at% Cr-doped NiO hierarch

This feature article focuses on recent research progress in noble metal@metal oxides core@shell NPs for gas sensor applications.

Semiconductor gas sensors using metal oxides, carbon nanotubes, graphene-based materials, and metal chalcogenides have been reviewed from the viewpoint of the sensitive, selective, and reliable detection of exhaled biomarker gases, and perspectives/strategies to realize breath analysis on a chip for disease diagnosis are discussed and suggested.

Au@NiO yolk-shell nanoparticles (NPs) were synthesized by simple solution route and applied for efficient gas sensor towards H₂S gas. Carbon encapsulated Au (Au@C core-shell) NPs were synthesized by glucose-assisted hydrothermal method, whereas Au@NiO yolk-shell NPs were synthesized by precipitation method using Au@C core-shell NPs as a template. Sub-micrometer Au@NiO yolk-shell NPs were formed having 50-70 nm Au NPs at the periphery of NiO shell (10-20 nm), which was composed of 6-12 nm primary

A monolayer α-Fe₂O₃inverse opal film with single-crystalline rotocenters shows reversible NO₂p–n sensing switches tuned by a<italic>T</italic>–<italic>C</italic>transition diagram.