Hokkaido University · 材料科学
H. Habazaki教授の研究室では、アルミニウム合金の陽極酸化挙動に注目し、特に酸化被膜形成時に合金成分が界面でどのように挙動するかを、モデル二元合金を用いた実験を通じて解明しています。特に、酸化被膜下に形成される数ナノメートル程度の成分富化層の生成機構に焦点を当てており、バリア型および多孔性陽極酸化膜の両方に共通するメカニズムの解明を目指しています。
Figures are computed from collected data and may differ slightly.
SummaryThe anodic oxidation of aluminium alloys is reviewed and discussed with reference to recent results of the authors on the anodizing of model binary aluminium alloys. Attention is given primarily to the oxidation of alloying elements at the alloy/film interface during the formation of barrier-type anodic films. However, the findings are also considered to be applicable to the formation of porous anodic films. The enrichments of alloy layers of about 1–5 nm thickness is revealed to be a rel