Professor Yeon-Gil Jung's research lab specializes in the development and mechanical evaluation of advanced ceramic materials, with a focus on dental ceramics and high-temperature structural ceramics. The lab investigates damage mechanisms, strength degradation, and fracture behavior under cyclic loading, particularly in bilayer and multi-phase ceramic systems relevant to dental restorations and investment casting cores. Key research directions include the design of novel ceramics with enhanced toughness and thermal stability through entropy stabilization and microstructural engineering.
Figures are computed from collected data and may differ slightly.
The hypothesis under examination in this paper is that the lifetimes of dental restorations are limited by the accumulation of contact damage during oral function; and, moreover, that strengths of dental ceramics are significantly lower after multi-cycle loading than after single-cycle loading. Accordingly, indentation damage and associated strength degradation from multi-cycle contacts with spherical indenters in water are evaluated in four dental ceramics: "aesthetic" ceramics-porcelain and mi
Natural teeth (enamel/dentin) and most restorations are essentially layered structures. This study examines the hypothesis that coating thickness and coating/substrate mismatch are key factors in the determination of contact-induced damage in clinically relevant bilayer composites. Accordingly, we study crack patterns in two model "coating/substrate" bilayer systems conceived to simulate crown and tooth structures, at opposite extremes of elastic/plastic mismatch: porcelain on glass-infiltrated
An entropy-stabilization strategy was applied to engineer a novel thermal insulating material by establishing a single-phase solid solution with the formula of (Y1/2Yb1/2)2(Ti1/3Zr1/3Hf1/3)2O7 (YYHEO). Structural analysis revealed that this material exceeded the typical substitutional solubility limit, even with a significant atomic size difference, where the conventional determination rule was defied. YYHEO exhibited a lower glass-like thermal conductivity due to its highly disordered crystal s
All-ceramic crowns are coming into widespread use because of their superior esthetics and chemical inertness. This study examines the hypothesis that glass-infiltrated alumina and spinel core ceramics are resistant to damage accumulation and strength degradation under representative oral contact conditions. Accordingly, Hertzian indentation testing with hard spheres is used to evaluate damage accumulation in alumina and spinel ceramics with different pre-form grain morphologies and porosities. I