이해석 교수

Perovskite solar cells have great potential for high efficiency generation but are subject to the impact of external environmental conditions such as humidity, UV and sun light, temperature, and electric fields. The long-term stability of perovskite solar cells is an important issue for their commercialization. Various studies on the stability of perovskite solar cells are currently being performed; however, the stability related to electric fields is rarely discussed. Here the electrical stabil

Abstract The status and problems of upscaling research on perovskite solar cells, which must be addressed for commercialization efforts to be successful, are investigated. An 804 cm 2 perovskite solar module has been reported with 17.9% efficiency, which is significantly lower than the champion perovskite solar cell efficiency of 25.2% reported for a 0.09 cm 2 aperture area. For the realization of upscaling high‐quality perovskite solar cells, the upscaling and development history of conventiona

Copper has attracted significant interests as an abundant and low‐cost alternative material for flexible transparent conducting electrodes (FTCEs). However, Cu‐based FTCEs still present unsolved technical issues, such as their inferior light transmittance and oxidation durability compared to conventional indium tin oxide (ITO) and silver metal electrodes. This study reports a novel technique for fabricating highly efficient FTCEs composed of a copper ultrathin film sandwiched between zinc oxides

The silicon surface texture significantly affects the current density and efficiency of perovskite/silicon tandem solar cells. However, only a few studies have explored fabricating perovskite on textured silicon and the effect of texture on perovskite films because of the limitations of solution processes. Here we produce conformal perovskite on textured silicon with a dry two-step conversion process that incorporates lead oxide sputtering and direct contact with methyl ammonium iodide. To separ

A highly efficient light-scattering layer based on a silica nanoparticle array was fabricated on a flexible polymer substrate by employing a direct vacuum deposition process at room temperature, facilitating a power conversion efficiency of 7.42% from a flexible organic solar cell.

The development of highly efficient flexible transparent electrodes (FTEs) supported on polymer substrates is of great importance to the realization of portable and bendable photovoltaic devices. Highly conductive, low-cost Cu has attracted attention as a promising alternative for replacing expensive indium tin oxide (ITO) and Ag. However, highly efficient, Cu-based FTEs are currently unavailable because of the absence of an efficient means of attaining an atomically thin, completely continuous

This study evaluated the impact of partial shading on CuInxGa(1-x)Se2 (CIGS) photovoltaic (PV) modules equipped with bypass diodes. When the CIGS PV modules were partially shaded, they were subjected to partial reverse bias, leading to the formation of hotspots and a possible occurrence of junction damage. In a module with a cadmium sulfide buffer layer, hotspots and wormlike defects were formed. The hotspots were formed as soon as the modules were shaded; the hotspots caused permanent damage (w

Carbon nanotube electrode–laminated perovskite solar cells in combination with n‐type tunnel oxide–passivated contact silicon solar cells demonstrate a high power conversion efficiency (PCE) of 24.42% when stacked in tandem. This is compared with conventional indium tin oxide/MoO x ‐deposited perovskite solar cells which give an efficiency of 22.35% when stacked in the same four‐terminal tandem system. Despite higher transmittance of the carbon nanotube electrode than that of the indium tin oxid

Electrodes for flexible supercapacitors were fabricated from manganese-doped carbon nanofibers (Mn-CNF) decorated with carbon-coated Co-CoO x (C/Co-CoO x ) nanotubes. The Mn-doped polyacrylonitrile (PAN)–2-methylimidazole (2MI) solution was electrospun using optimized Mn concentrations and ZIF-67 was then surface loaded by wet impregnation with added polyvinylpyrrolidone (PVP). These ZIF-67 loaded Mn-fibers, when annealed, resulted in carbon-coated C/Co-CoO x nanotubes on the Mn-CNF surface. In