We measured the elastic modulus of individual multiwalled carbon nanotubes (MWCNTs) grown by catalytic chemical vapor deposition (CVD) over a broad diameter range (10-25 nm). Alternating current (ac) dielectrophoresis was used for efficient tube deposition, and atomic force microscope (AFM) force-displacement curve technique was used for stiffness measurements. The elastic modulus exhibits a strong diameter dependence, showing a difference of nearly 2 orders of magnitude in the 10-20 nm diameter

We investigated the water contents in several organ tissues such as the liver, spleen, kidney, and brain tissue of rats using the terahertz spectroscopic imaging technique. The water contents of the tissues were determined by using a simple equation containing the absorption coefficients of fresh and lyophilized tissues and water. We compared the measured water contents with the difference in mass of tissues before and after lyophilization. All results showed a good match except for the kidney,

수행평가는 피험자의 반응을 평가하기 위한 채점자의 개입을 필요로 하는 평가형태로 채점자는 평가 결과에 영향을 주는 주된 요인이 된다. 일반적으로 채점자의 개입으로 인해 수행평가 결과의 신뢰도는 낮아지게 되고, 낮은 신뢰도는 수행평가 결과의 활용을 제한하는 요인으로 작용하게 된다. 특히 수행평가 결과를 선발과 같은 고부담(high-stakes) 의사결정에 활용할 경우, 수행평가 결과의 신뢰도 검증은 보다 중요한 이슈가 된다. 이 연구는 현재 학교 현장에서 보편적인 수행평가 채점 방식인 교과 담당 교사의 전담 채점 방식의 낮은 신뢰도 문제를 보완하기 위해 학생들의 동료평가를 활용하는 채점 방식을 연구하였다. 이러한 연구목적을 위해 일반화가능도 이론이 적용되어 학교 현장에서 수행평가에 영향을 주는 요소들의 상대적인 영향력이 분석되었고, 적정 수준의 일반화가능도 계수를 확보하기 위한 효율적인 측정구조가 검토되었다. 학생 동료평가 방식의 타당성을 검토하기 위해 학생들의 동료평가 결과와 교사의

Abstract We propose an all-solid-state Na ion-based synaptic transistor (NST) to overcome the low retention problem of the Li ion-based synaptic transistor (LST). Through our analysis, it was found that the retention instability in an ionic synaptic transistor originated from its high ionic diffusivity. As confirmed by cyclic voltammetry analysis, Na ions have a lower ionic diffusivity than Li ions in the WO x layer. The state retention of NST was found to be improved to 20 times that of LST. Fu

Uniformly dispersed deposition of various nanoparticles (gold and silver of 20–50nm) and nanowires (ZnO and VOx) on different surfaces (Si, GaAs, mica, and steel) was obtained by boiling colloid drops on preheated substrates. Our results suggest a deposition mechanism based on the formation of microdrops induced by boiling. Indeed, microdrops produced by an ink-jet printing system resulted in uniformly dispersed deposits when the substrate was heated to high temperatures. We demonstrate that boi

본 연구는 가상강좌에 사용될 수 있는 강의 평가 도구를 개발하고 이를 타당화하는데 목적이 있다. 연구대상은 2005년 1학기에 개설된 K대학의 가상강좌를 수강하는 학부생들이며 예비검사를 위해 406명이 참여하였고, 본 검사에서는 2,020명이 참여하여 이 중 불성실한 응답을 제외한 1,678명의 자료를 최종 분석에 포함하였다. 가상강의 평가 도구의 개발을 위해 먼저 선행연구를 토대로 4개의 평가영역을 규명하고 영역별로 총 15개의 평가문항을 개발하였다. 개발된 평가문항을 이용하여 예비검사를 실시하였고, 문항 분석결과를 토대로 4개 영역에서 총 13개의 평가문항을 추출하였다. 확정된 최종 평가 문항으로 본 검사를 실시한 후 강의평가 도구의 타당화를 검증하였다. 분석 결과, 문항난이도와 변별도, 문항 제거시 신뢰도, 내적 일관성 신뢰도가 양호한 것으로 나타났으며, 일반화가능도 이론의 G-연구를 적용하여 평가 점수의 분산 비율을 추정해 본 결과, 교수자에 속한 학생들의 분산과 잔차 분산이

Abstract In this study, we investigated the effect of an Al 2 O 3 barrier layer in an all-solid-state inorganic Li-based nano-ionic synaptic transistor (LST) with Li 3 PO 4 electrolyte/WO x channel structure. Near-ideal synaptic behavior in the ultralow conductance range (∼50 nS) was obtained by controlling the abrupt ion migration through the introduction of a sputter-deposited thin (∼3 nm) Al 2 O 3 interfacial layer. A trade-off relationship between the weight update linearity and on/off ratio

Abstract Conjugated polymers based on cyclopentadithiophene (CPDT) moieties are widely used in optoelectronics applications but rarely in field‐effect transistors (FETs). This is due to the steric hindrance at the tetrahedral center of the CPDT core, which is a critical problem requiring resolution without diminishing the polymer crystallinity and solubility. A bulky CPDT‐based high‐mobility copolymers are synthesized here, which shows excellent π–π stacking in the film states with good solubili

『한국교육종단연구2005』에서는 매년 학생들의 학년별 성취도 변화를 평가하도록 우리나라에서는 처음으로 국가수준 학업성취도 평가에서 수직척도가 개발되어 적용되었다. 이 연구는『한국교육종단연구2005』에서 개발된 수직척도의 타당성을 검토하고자 (연구) 설계되었고, 2005년 이후 4년 간 누적된 자료를 이용하여 척도화 표본과 표준화 표본을 통합하여 분석하였다. 수직척도의 타당성을 검토하기 위해, 6가지 서로 다른 수직척도 개발 방법을 선정하여 국어, 수학, 영어 교과에 적용하였고, 다층분석 기법을 적용하여 수직척도화 방법을 비교하였다. 분석 결과, 문항반응이론을 적용하기 위한 표본의 사례 수 제한과 그로 인한 모수추정의 불안정성 문제, 학년 간에 100점이라는 임의 성장 정보를 추가한 문제, 차별적으로 기능하는 문항을 학년 간 수직척도 개발을 위한 공통문항으로 사용한 문제, 문항 반응 패턴 채점 방식이 아닌 총점과 수직척도 점수 변환 방식을 사용한 문제 등은 개발된 수직척도의 타당성을

이 연구는 초등학교 과학과 수행평가에서 총체적 채점과 분석적 채점 방식이 검사 점수의 일반화가능도에 미치는 영향을 분석하기 위하여 주요 요인들의 상대적 영향력과 총체적 채점과 분석적 채점 방식이 신뢰도에 미치는 영향을 분석하고, 수행평가 채점의 효율적인 측정조건을 탐색하였다. 초등학교 학생을 대상으로 과학과 수행평가를 시행하고 총체적 채점과 분석적 채점 방식으로 3명의 교사가 각각 점수를 부여하였다. 이 연구를 통해 도출된 결론은 다음과 같다. 첫째, 분석적 채점 방식이 총체적 채점 방식보다 신뢰로운 채점 결과를 산출할 수 있다는 전통적인 설명과 주장은 일반화가능도 이론을 적용한 이 연구에서는 지지되지 않았다. 오히려 이러한 주장은 Cronbach α와 같이 수행평가의 채점 방식을 적합하게 반영하지 못하는 신뢰도 추정 방법을 적용함으로써 생기는 오해일 수 있다. 둘째, 과학과 수행평가 채점의 경우, 분석적 채점과 총체적 채점은 비슷한 수준의 일반화가능도 계수를 산출했고, 그 이유는

We have achieved 21% large-area conversion efficiency with PERL (passivated emitter, rear locally diffused) solar cells featuring plated front contacts. Industrial 156 mm p-type Czochralski single-crystalline silicon wafers were used as substrates. Our cells employ a single-side texture, a single-side emitter, and a double-layer anti-reflective coating composed of PECVD silicon nitride and thermal silicon oxide layers. The rear side is passivated with a dielectric stack (Al 2 O 3 –SiO x N y ), a

High-pressure hydrogen annealing (HPHA) treatment is an effective hydrogen doping method to improve electrical characteristics and stability of InGaZnO (IGZO) thin film transistors (TFTs). The HPHA effects on IGZO TFTs under various pressure conditions were investigated using analytical techniques. Drive current, field effect mobility, subthreshold swing, and bias stress stability of IGZO TFTs were significantly improved as the HPHA pressure was increased up to 20 atm. To analyze the performance