Perovskite solar cells have great potential for high efficiency generation but are subject to the impact of external environmental conditions such as humidity, UV and sun light, temperature, and electric fields. The long-term stability of perovskite solar cells is an important issue for their commercialization. Various studies on the stability of perovskite solar cells are currently being performed; however, the stability related to electric fields is rarely discussed. Here the electrical stabil

Abstract Organic-inorganic hybrid perovskite solar cells (PSCs) have been extensively studied because of their outstanding performance: a power conversion efficiency exceeding 22% has been achieved. The most commonly used PSCs consist of CH 3 NH 3 PbI 3 (MAPbI 3 ) with a hole-selective contact, such as 2,2′,7,7′-tetrakis( N , N -di- p -methoxyphenylamine)-9,9-spiro-bifluorene (spiro-OMeTAD), for collecting holes. From the perspective of long-term operation of solar cells, the cell performance an

Vertically aligned CdTe nanorods were fabricated by electrodeposition and were applied for the active layer of solar cells after being combined with poly(3-octylthiophene) (P3OT), a conjugated polymer. The electrodeposited CdTe showed an n-type behavior with the electric resistivity and the electron density of 2×106Ωcm, 1.3×1010cm−3, respectively. Quantum efficiency curve of the hybrid solar cells exhibited a peak at the same wavelength as the optical absorption for CdTe nanorods. The hybrid sol

Graphene quantum dot (GQD) layers were deposited as an energy-down-shift layer on crystalline-silicon solar cell surfaces by kinetic spraying of GQD suspensions. A supersonic air jet was used to accelerate the GQDs onto the surfaces. Here, we report the coating results on a silicon substrate and the GQDs' application as an energy-down-shift layer in crystalline-silicon solar cells, which enhanced the power conversion efficiency (PCE). GQD layers deposited at nozzle scan speeds of 40, 30, 20, and

Hybrid tandem solar cells offer the benefits of low cost and full solar spectrum utilization. Among the hybrid tandem structures explored to date, the most popular ones have four (simple stacking design) or two (terminal/tunneling layer addition design) terminal electrodes. Although the latter design is more cost-effective than the former, its widespread application is hindered by the difficulty of preparing an interface between two solar cell materials. The oldest approach to the in-series bond

This study evaluated the impact of partial shading on CuInxGa(1-x)Se2 (CIGS) photovoltaic (PV) modules equipped with bypass diodes. When the CIGS PV modules were partially shaded, they were subjected to partial reverse bias, leading to the formation of hotspots and a possible occurrence of junction damage. In a module with a cadmium sulfide buffer layer, hotspots and wormlike defects were formed. The hotspots were formed as soon as the modules were shaded; the hotspots caused permanent damage (w

Solar energy has gained prominence because of the increasing global attention received by renewable energies. This shift can be attributed to advancements and innovations in solar cell technology, which include developments of various photovoltaic materials, such as thin film and tandem solar cells, in addition to silicon-based solar cells. The latter is the most widely commercialized type of solar cell because of its exceptional durability, long-term stability, and high photoconversion efficien

In the photovoltaic (PV) industry, module manufacturers have begun to install bifacial cells into monofacial modules because of their lower production costs relative to monofacial cells. This is linked mainly to a 65.3% reduction in rear aluminum paste consumption and the corresponding 0.5 cent/wafer cost reduction for M4 (161.7 × 161.7 mm2) size wafers. Therefore, this study compared the performance of monofacial PV modules with the monofacial cells as a reference group and bifacial cells as th

Recently, titanium oxide has been widely investigated as a carrier-selective contact material for silicon solar cells. Herein, titanium oxide films were fabricated via simple deposition methods involving thermal evaporation and oxidation. This study focuses on characterizing an electron-selective passivated contact layer with this oxidized method. Subsequently, the SiO2/TiO2 stack was examined using high-resolution transmission electron microscopy. The phase and chemical composition of the titan

Radio frequency (RF) magnetron-sputtered TiO2 (RS-TiO2) is investigated as a hole-blocking layer for perovskite solar cells. RS-TiO2 shows conformal, dense, and efficiently electron transferable properties. Power conversion efficiency (PCEs) of 20.9% were obtained with high reproducibility. RS-TiO2 also showed potential in the up-scaling process, transparent perovskite, and perovskite/silicon 4-terminal tandem solar cells. With increasing active area 40 times from 0.075 cm2 to 3 cm2 without divi

This review discusses the use of evaporation, chemical vapor deposition, and sputtering as the three main dry deposition techniques currently available for fabricating perovskite solar cells. We outline the distinct advantages that each method offers in terms of film quality, control, and scalability. Additionally, recent advancements in process optimization and the integration of dry deposition with other fabrication techniques are highlighted. Thus, this review provides valuable insights into